This paper presents the general influence of feed rate on residual surface stresses of carbon steel in high-feed face milling. Residual stresses were measured using the X-ray diffraction technique. The feed per tooth was realised up to 8 mm per tooth. It was conducted that tensile residual stresses are generated when high-feed face milling. Increasing feed rate leads to higher tensile surface residual stresses in the face milling of carbon steel.
Surface Residual Stresses in High-Feed Face Milling of Carbon Steel
Lect.Notes Mechanical Engineering
Vehicle and Automotive Engineering ; 2022 ; MISKOLC, Hungary September 08, 2022 - September 09, 2022
2022-09-10
6 pages
Aufsatz/Kapitel (Buch)
Elektronische Ressource
Englisch
Probabilistic Prediction of Burr Patterns of 1045 Carbon Steel in Face Milling
British Library Online Contents | 2002
|Metallurgical Instability and Residual Stresses in Hardened Steel
SAE Technical Papers | 1971
|Distortion and Residual Stresses in Nitrocarburized and Carbonitrided SAE 1010 Plain Carbon Steel
SAE Technical Papers | 2008
|