The applications of fused deposition modelling (FDM) based 3D printing have gone beyond merely simple prototypes to where functionalities are expected. One of such functionalities is the water retention properties, especially for fluid handling products, either completely waterproof or deliberately porous. Issues arise especially in determining crucial parameters and their optimization to achieve the desired water retention properties. This study established the relationship among printing parameters (layer thickness and wall thickness) and water temperature with leakage flow rate. A series of 3D printed polylactic acid (PLA) vessels were fabricated at various layer height and wall thickness. Then, the volumetric loss of water at various temperatures was measured, elapsed time was recorded, and the leakage flow rate was calculated for each 3D printed vessel. It has been found that the leakage flow rate decreased when layer height decreased, wall thickness increased, and water temperature decreased. Based on multilinear regression analysis, the magnitude of influence for the layer height was the highest, which could reach at a point where variation in wall thickness and water temperature had no effect. A regression model having 81.27% fitness that provided a quantitative relationship among all parameters had also been obtained. ANOVA analysis revealed that all parameters were statistically significant in optimizing as well as predicting the value of the leakage flow rate.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Water Retention Properties of a Fused Deposition Modeling Based 3D Printed Polylactic Acid Vessel


    Weitere Titelangaben:

    Adv Struct Mater




    Erscheinungsdatum :

    2022-01-10


    Format / Umfang :

    13 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Process Calibration for Elastically Scaled 3D Printed Models Using Fused Deposition Modeling

    Taylor, Robert M. / Mares, Edgar / Rane, Rhugdhrivya et al. | AIAA | 2019


    Development of Materials for Fused Deposition Modeling

    Smith, J. G., Jr. / Shanahan, M. H. / Siochi, E. J. | NTRS | 2015