The modern understanding of the strength of bodies with cracks under statically and cyclically varying loads makes it possible to calculate the residual life of a structure, however, the specific conditions of deformation of a railway rail require the development of new methods for studying the initiation and development of fatigue cracks. herefore, the analysis of the laws of crack development is of great importance. Cracks begin to develop long before complete failure during fatigue, plastic, and even brittle failure. The duration of the destruction process, i.e. crack growth until complete destruction takes up a significant part of the “life” of the part, reaching 90% and more. The main thing during the operation of a part is not the presence of a crack, but the rate of its growth. In this work, a microstructural analysis of the cross-sectional surface of five rails with internal cracks, longitudinal and transverse, is carried out. Rail samples taken out of operation after many years of service. Fractographic analysis of the crack surface and the surrounding material indicates a significant degradation of the physical and mechanical properties of the rail steel.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Features of Structure Formation of Rail Steel with Internal Cracks in Long-Term Operation


    Weitere Titelangaben:

    Lect. Notes in Networks, Syst.


    Beteiligte:
    Manakov, Aleksey (Herausgeber:in) / Edigarian, Arkadii (Herausgeber:in) / Atroshenko, Svetlana (Autor:in) / Smirnov, Vladimir (Autor:in) / Maier, Sergei (Autor:in)

    Kongress:

    International Scientific Siberian Transport Forum ; 2021 May 11, 2021 - May 14, 2021



    Erscheinungsdatum :

    2022-03-19


    Format / Umfang :

    11 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Features of Structure Formation of Rail Steel with Internal Cracks in Long-Term Operation

    Atroshenko, Svetlana / Smirnov, Vladimir / Maier, Sergei | TIBKAT | 2022


    Long steel rail transportation operation vehicle set

    YANG SHIWEI / PENG LIAO / LI YAN et al. | Europäisches Patentamt | 2020

    Freier Zugriff

    Scanning device for steel rail bottom transverse cracks

    MA ZHANSHENG / WU XING / QIN LICHAO et al. | Europäisches Patentamt | 2016

    Freier Zugriff

    Rail To prevent cracks Rail Joint

    LIM GI TAEK | Europäisches Patentamt | 2019

    Freier Zugriff

    Steel rail operation vehicle set

    JIA TIANNING / HAO SHANSHAN / SHENG MANMAN | Europäisches Patentamt | 2022

    Freier Zugriff