Abstract The urging need to reduce the harmful emissions required a thorough investigations into the methods of utilizing the dissimilar lightweight materials in modern automobile, aviation and marine industries. With the exception use of dissimilar materials, traditional joining methods become limited or incapable to maintain safety standards. The adhesive bonding, therefore, seems an ideal choice to overcome this limitation due to uniform stress distribution, fatigue resistance and sound isolation. However, the role of environmental degradation become vital in the areas where the joints exposed directly or indirectly to the sunlight, humidity and extreme change in the temperature. With such key industries, intensive work to comply with safety standards are crucial. The current work devoted to examining the influence of Ultra-Violet (UV) exposure on three different Carbon Fiber Reinforced Polymer (CFRP) setup of Aluminum-CFRP single lap joint with respect to strength and fracture mode. The samples exposed to the specified UV dosage of three exposure duration then tested mechanically based on ASTM standards. The outcomes indicate that the fracture modes are highly affected by the CFRP orientation as well as the UV exposure time. Moreover, the joint strength decreases with increases of the UV exposure time.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Influence of Different UV Exposure Time on the CFRP/Aluminum Single Lap Joints Strength and Fracture Modes


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2019-03-30


    Format / Umfang :

    9 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Influence of Different UV Exposure Time on the CFRP/Aluminum Single Lap Joints Strength and Fracture Modes

    Khaleel, Salah Mahdi / Rolfe, Bernard / Al-Ameri, Riyadh et al. | Online Contents | 2019



    Influence of harsh environmental conditions on CFRP-aluminum single lap joints

    Breziner, Luis / Hutapea, Parsaoran | Emerald Group Publishing | 2008


    Strength Analysis of CFRP Composite Material Considering Multiple Fracture Modes

    Bruyneel, Michael / Naito, Tadashi / Urushiyama, Yuta | SAE Technical Papers | 2015


    Cryogenic Mode-I Fracture Behavior of Film Adhesive in CFRP & Aluminum Bond Joints

    He, J. / Aoki, T. / Shimoda, T. et al. | British Library Conference Proceedings | 2004