Diffusion welding is done on specimens of duplex stainless steel and low carbon steel under varied temperature and holding time. The specimens were clamped using jigs and pre-pressed at 10 MPa and heated in a furnace. Impact test were performed on the joined samples. The effect of process temperature and holding time on the impact strength of the diffusion welds were observed. The impact strength of the joints was examined, and the highest value of 0.9 J is obtained at a temperature of 1050 °C and holding time of 240 min.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Effect of Process Temperature and Holding Time on Weldability in Diffusion Welding of Duplex Stainless Steels and Marine Grade Steels for Oil and Gas Pipes


    Weitere Titelangaben:

    Adv Struct Mater


    Beteiligte:

    Erschienen in:

    Design in Maritime Engineering ; Kapitel : 27 ; 359-364


    Erscheinungsdatum :

    2022-02-15


    Format / Umfang :

    6 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Weldability of Maraging steels

    Ryban, D. | British Library Online Contents | 1992



    Weldability of high strength steels in wet welding conditions

    Fydrych, Dariusz / Łabanowski, Jerzy / Rogalski, Grzegorz | Online Contents | 2013


    Duplex stainless steels for offshore use

    Bendall, K. | Tema Archiv | 1992


    Duplex stainless steels for chemical tankers

    Charles, J. / Vincent, B. | Tema Archiv | 1997