In this work, ZrC-based composites reinforced with SiC particles were processed using the hot-pressing route. The influence of SiC content on the microstructure and mechanical properties of the hot-pressed composites was investigated. In all composites with different SiC contents, the highest relative density was obtained for ZrC-based composite containing 20 vol% SiC, having a value of 97 per cent. The flexural strength of ZrC-based composites increased modestly from 390 to 452 MPa as the SiC content increased from 10 to 20 vol%. The increase in strength was attributed to a decrease in grain size and improvement of the relative density. But the strength did not show great variation when the content of the SiC particles increased to 30 vol%, which may be because of the inhomogeneous microstructure and the low relative density. In contrast, toughness and hardness did not vary significantly with SiC content.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fabrication of hot-pressed ZrC-based composites


    Beteiligte:
    Ma, B (Autor:in) / Zhang, X (Autor:in) / Han, J (Autor:in) / Han, W (Autor:in)


    Erscheinungsdatum :

    2009-08-01


    Format / Umfang :

    5 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Pressed pistons

    Engineering Index Backfile | 1943


    Pressed pistons

    Engineering Index Backfile | 1943


    Pressed component manufacturing method, pressed component, and press apparatus

    KUBO MASAHIRO / YOSHIDA HIROSHI / MIYAGI TAKASHI | Europäisches Patentamt | 2019

    Freier Zugriff

    LCO Flutter Analysis on Coir Pressed Mat Fibre/Epoxy Composites Plate

    Rahman, M.A.A. / Rafie, A.S.M. / Varatharajoo, R. | British Library Conference Proceedings | 2014