Provision of a layer of zinc on aluminium to provide the fillets for soldering is well established but this usually necessitates a thick layer of zinc (>30μm) and soldering at temperatures below 450°C.New technology has been developed to enable sound joints to be made on aluminium heat exchangers using a much thinner layer of zinc (4 to 8 μm typically) on the aluminium component to provide the joint. By the correct combination of flux and zinc coating thickness, joints have been obtained over a wide range of heating conditions.Preferred temperature cycles are similar to those used by the industry today for brazing of Aluminium:Silicon braze-clad aluminium components which should facilitate tranfer by industry to the new technology.
Zinc Brazing of Automotive Aluminum Heat Exchangers
Sae Technical Papers
International Congress & Exposition ; 1993
1993-03-01
Aufsatz (Konferenz)
Englisch
Zinc brazing of automotive aluminum exchangers
Kraftfahrwesen | 1993
|Nocolok Brazing Aluminum Heat Exchangers
British Library Conference Proceedings | 1995
|Nocolok Brazing Aluminum Heat Exchangers
SAE Technical Papers | 1995
|Nocolok brazing aluminum heat exchangers
Kraftfahrwesen | 1995
|Inert Atmosphere Fluxless Brazing of Aluminum Heat Exchangers
SAE Technical Papers | 1988
|