Composites are wonderful materials that have revolutionized the field of engineering because they can provide more versatility when compared to other materials and can be tailored to have maximum strength and stiffness. Experimental investigation was carried out to study the influence of fiber volume fraction, fiber length and percentage of fillers on fracture toughness ,fracture energy and impact energy of glass fiber reinforced composite. Panels with different configurations were made using fiber glass chopped strand mat and unidirectional roving with epoxy resin. Wet Hand Layup method was adopted for fabrication of panels with different fiber volume fractions and filler density while Bulk Molding Compound Technique was used for making panels with different fiber lengths. ASTM D-5045-14 was consulted for the development of test specimens to conduct flexural testing of these panels. The analysis based on the experimental results obtained shows that fracture toughness and fracture energy increases with increase in fiber volume fraction and fiber length while it decreases with the increase of percentage of fillers in composites.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of Fiber Volume Fraction, Fiber Length and Fillers on Fracture Toughness, Impact Toughness and Fracture Energy of Glass Fiber Composite Panels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Tehami, Ahmad Waqar (Autor:in) / Ali, Haseeb (Autor:in)

    Kongress:

    WCX World Congress Experience ; 2018



    Erscheinungsdatum :

    2018-04-03




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Interlaminar fracture toughness of carbon/flax fiber hybrid composite

    YUAN Weike / LI Yan / ZHAO Jian | DOAJ | 2022

    Freier Zugriff

    Interfacial Fracture Toughness of Carbon Fiber Reinforced Composites

    XIE Zonghong / CAI Shujie / GUO Qi et al. | DOAJ | 2018

    Freier Zugriff


    The fracture toughness of a fiber reinforced polymeric film

    Tielking, John / Thomas, V. | AIAA | 1996


    Fiber Reinforced Fire Resistant Syntactic Foam and Its Fracture Toughness Characterization

    Panduranga, Raghu / Sharpe, Matthew / Shivakumar, Kunigal | AIAA | 2009