To protect ship equipment of river and sea transport, it is suggested to use polymeric protective coatings based on epoxy diane oligomer ED-20, polyethylene polyamine (PEPA) curing agent and filler, which is a departure from industrial production. Thus the purpose of the work is analysis of major dependency of the properties on the content of fillers that allowed to revealed the critical filler content (furnace black) in composites to form a protective coating with the required set of characteristics. The infrared (IR) spectral analysis was used to investigate the presence of bonds on the surface of particles of the PM-75 furnace black, which allows us to assess the degree of cross-linking of the polymer. The influence of the content of dispersed furnace black on the physicomechanical and thermophysical properties and the structure of the protective coating is investigated. For the formation of the coating with increased adhesive properties, the optimum content of the additive is q = 25 parts by weight (pts.wt.), due to the increase in the number of C—O, C—C, C═O, C═C, C═O, and O═C—H bonds. For the formation of the coating with increased cohesive properties, the optimum content of the additive is q = 20 pts.wt., which is associated with the maximum compaction of the polymer spatial net. On the basis of the analysis of the surface of the composite fracture, a homogeneous topology of the fracture surface was found which characterizes the viscous state of material destruction at the content of the additive q = 5 pts.wt., which provides significant improvement of the physical and mechanical properties of the materials developed. Additionally, it was found that when the PM-75 particles were introduced at the content of q = 10-30 pts.wt., the uniformity of the structure is retained, but its abnormal similarity is observed. This allowed us to determine the optimal content of the additive (q = 20 pts.wt.) for the formation of coatings with high cohesive strength in the complex.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Influence of the Content and Nature of the Dispersive Filler at the Formation of Coatings for Protection of the Equipment of River and Sea Transport


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:


    Erscheinungsdatum :

    2020-01-23


    Format / Umfang :

    11 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Heat-moderating filler for intumescent coatings

    Sawko, P. M. / Riccitiello, S. R. | NTRS | 1977


    Resistance to Impact of Loads of Shock Nature of Protective Coatings Intended for Protection of Boat Devices of Water Transport

    Buketov, Andriy / Sapronov, Oleksandr / Menou, Abdellah et al. | Springer Verlag | 2022




    Advective dispersive contaminant transport towards a pumping well

    Kooten, Jaco Johannes Adriaan | Katalog Agrar | 1996