The focus of this study was to determine the residual stress and retained austenite profiles for carbonitrided and nitrocarburized SAE 1010 plain carbon steel and to relate these profiles to one another and to the distortion resulting from heat treatment. Navy C-ring specimens were used for the purpose of this study and X-ray diffraction techniques were used to measure both residual stress and retained austenite. The findings from this research are then applied to a manufacturing application involving the surface hardening of a thin shelled, plain carbon steel automotive component.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Distortion and Residual Stresses in Nitrocarburized and Carbonitrided SAE 1010 Plain Carbon Steel


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:
    Northwood, Derek O. (Autor:in) / Bauerle, Peter (Autor:in) / Bowers, Randy (Autor:in) / Campagna, Victoria (Autor:in) / Sun, Xichen (Autor:in)

    Kongress:

    SAE World Congress & Exhibition ; 2008



    Erscheinungsdatum :

    2008-04-14


    Format / Umfang :

    7 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    2008-01-1421 Distortion and Residual Stresses in Nitrocarburized and Carbonitrided SAE 1010 Plain Carbon Steel

    Campagna, V. / Bowers, R. / Northwood, D.O. et al. | British Library Conference Proceedings | 2008




    Ferritic Nitrocarburizing of SAE 1010 Plain Carbon Steel Parts

    Northwood, Derek O. / Manivannan, Madhavan / Stoilov, Vesselin | SAE Technical Papers | 2015