CFRP(Carbon Fiber Reinforced Plastics) is applied for many parts in aerospace vehicle and automobiles. The strength is already improved by chemical fiber treatment. In this study, the improvement of physical surface treatment to mechanical properties is focused. Three kinds of grain-degrees of sand papers are used for physical surface treatment to plain woven carbon cloth. The rubber particle modification method is also used for examining the improvement of strength. DCB(Double Cantilever Beam) test and static bending test are conducted. The relationships between fracture toughness, bending strength and rubber content, grain degree are examined. The relationships between crack propagation length and grain degree is also examined. The observation of carbon fiber is also conducted using SEM (Scanning Electron Microscope). As a result, it is understood that the rubber modification and physical surface treatment is effective for the strength of CFRP. The effect at tensile and compressive side to the strength is examined in detail.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Physical Surface Treatment of Carbon Fiber on Fracture Toughness and Bending Properties for CFRP


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE 2005 World Congress & Exhibition ; 2005



    Erscheinungsdatum :

    2005-04-11




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Effect of Physical Surface Treatment of Carbon Fiber on Fracture Toughness and Bending Properties for CFRP

    Takemura, K. / Shiibashi, H. / Society of Automotive Engineers | British Library Conference Proceedings | 2005




    Interfacial Fracture Toughness of Carbon Fiber Reinforced Composites

    XIE Zonghong / CAI Shujie / GUO Qi et al. | DOAJ | 2018

    Freier Zugriff

    Interlaminar fracture toughness of carbon/flax fiber hybrid composite

    YUAN Weike / LI Yan / ZHAO Jian | DOAJ | 2022

    Freier Zugriff