Carburized parts often see use in powertrain components for the automotive industry. These parts are commonly quenched and tempered after the carburizing process. The present study compared the austempering heat treatment to the traditional quench-and-temper process for carburized parts. Samples were produced from SAE 8620, 4320, and 8822 steels and heat treated across a range of conditions for austempering and for quench-and-tempering. Distortion was examined through the use of Navy C-Ring samples. Microstructure, hardness, and Charpy toughness were also examined. X-ray diffraction was used to compare the residual stress found in the case of the components after the quench-and-temper and the austempering heat treatments. Austempering samples showed less distortion and higher compressive residual stresses, while maintaining comparable hardness values in both case and core. Toughness measurements were also comparable between both processes.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Comparison of Austempering and Quench-and-Tempering Processes for Carburized Automotive Steels


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:
    Clark, Andrew D. (Autor:in) / Northwood, Derek O. (Autor:in) / Bauerle, Peter (Autor:in) / Bowers, Randy J. (Autor:in) / Sun, Xichen (Autor:in)

    Kongress:

    SAE 2013 World Congress & Exhibition ; 2013



    Erscheinungsdatum :

    2013-04-08


    Format / Umfang :

    8 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Comparison of Austempering and Quench-and-Tempering Processes for Carburized Automotive Steels

    Clark, A.D. / Northwood, D.O. / Bowers, R.J. et al. | British Library Conference Proceedings | 2013


    Austempering Process for Carburized Low Alloy Steels

    Barber, Gary / Zou, Qian / Lumbreras, Rebeca et al. | SAE Technical Papers | 2013


    Strength and Ductility with Boron Quench Tempering Steels

    Weidner, H. C. | SAE Technical Papers | 1968


    CASE HARDENABILITY OF CARBURIZED STEELS

    SAE Technical Papers | 1997


    CASE HARDENABILITY OF CARBURIZED STEELS

    SAE Technical Papers | 1991