TS590N/mm2 hot rolled steel showing a good balance of stretch formability and stretch flangeability has been newly developed for manufacturing high strength automotive parts. A laboratory study revealed that an introduction of a small amount of martensite in ferrite · bainite microstructure remarkably improves uniform elongation of ferrite · bainite steel giving little influence on its good localized elongation. Characteristics in ductile property of this “Tri-Phase” type steel were confirmed in press forming tests.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Formability of TS590 N/mm2 “Tri-Phase” Hot Rolled Steel


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Shirasawa, H. (Autor:in) / Mimura, K. (Autor:in) / Inoue, N. (Autor:in) / Yokoi, T. (Autor:in) / Shibata, Z. (Autor:in)

    Kongress:

    International Congress & Exposition ; 1993



    Erscheinungsdatum :

    1993-03-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Evaluation of a New, Dual Phase, Cold Rolled Steel - Formability

    Stevenson, Robin / Brazier, William G. | SAE Technical Papers | 1978


    Evaluation of a new, dual phase, cold rolled steel-formability

    Brazier, W.G. / Stevenson, R. | Tema Archiv | 1978


    Evaluation of a New, Dual Phase, Cold-Rolled Steel- Formability

    Brazier,W.G. / Stevenson,R. / General Motors Res.Lab.,US | Kraftfahrwesen | 1978


    Formability of TS590 N/mm**2 "tri-phase" hot rolled steel

    Shirasawa,H. / Mimura,K. / Ykoi,T.,hibata,Z. et al. | Kraftfahrwesen | 1993


    590 N/mm2 tri-phase hot-rolled steel with good formability

    Mimura, K. / Yokoi, T. / Shirasawa, H. et al. | Tema Archiv | 1993