The current work investigates the hot corrosion demeanour of Hastelloy X weldment produced with autogenous mode through key-hole plasma arc welding (K-PAW). The hot corrosion test has been performed for weldment in molten salt-1 (MS-1) (75 % Na2SO4 + 25 % V2O5) and molten salt-2 (MS-2) (75 % Na2SO4 + 20 % V2O5 + 5 % NaCl) circumstance for 25 hrs (25 cycles) at 900 °C. The MS-1 substrate of both base metal and weldment provided the lowest weight gain than the MS-2 substrate. The NaCl in the MS-2 causes severe hot corrosion on the substrate, whereas the absence of NaCl in MS-1 reduces the hot corrosion effects. The highest parabolic constant is observed for K-PAW weldment in MS-2 condition. The tendency of hot corrosion rate follows the order of, Base Metal MS-1 < K-PAW MS-1 < Base Metal MS-2 < K-PAW MS-2. The occurrence of protective phases like chromium oxides (Cr2O3), spinel oxides (NiCr2O4 and NiFe2O4) Nickel oxide (NiO) on the substrate resist the further oxidation. But, the development of MoO3 and Fe2O3 phases are increased the cracking as well as spallation rate which promotes severe corrosion of the substrates. The plasma arc welded substrate and base metal in MS-1 condition are giving better resistance than in MS-2 at 900 °C.
Hot Corrosion Demeanour of Key-Hole Plasma Arc Welded Aerospace Grade Hastelloy X in Molten Salts Environment
Sae Int. J. Adv. and Curr. Prac. in Mobility
International Conference on Advances in Design, Materials, Manufacturing and Surface Engineering for Mobility ; 2020
Sae International Journal of Advances and Current Practices in Mobility ; 3 , 2 ; 823-830
2020-09-25
8 pages
Aufsatz (Konferenz)
Englisch
SAE Technical Papers | 2020
|Metallurgical examination of Hastelloy x for corrosion
TIBKAT | 1964
|Studies on Metallurgical and Mechanical Properties of Plasma Arc Welded Aerospace 80A Grade Alloy
SAE Technical Papers | 2020
|Metallurgical examination of Hastelloy x for corrosion
TIBKAT | 1964
|SAE Technical Papers | 2019
|