Molybdenum sulfide nanoparticles have been successfully obtained, for lubricant applications, by means of a wet chemical synthesis in an aqueous solution employing ammonium molybdate, citric acid and ammonium sulfide as the reactants. Some molybdenum-citrate complexes were formed and they reacted with the ammonium sulfide to form MoS₂ nanoparticles. Mo:citrate molar ratio was identified as being the most relevant of the synthesis parameters that affected the phase and morphology of the final products. The optimized nanopowders were softly agglomerated and amorphous, with a mean size of the primary particles of about 30 nm. The compatibility between the thus obtained MoS₂ nanopowders and some commercial after-treatment catalysts for diesel vehicle engines was tested. Diesel oxidation, soot combustion and ammonia-SCR de-NOx catalysts were considered as were the possible effects on the catalytic activity and their possible reaction to the MoS₂ additive. In general, the presence of the MoS₂ nano-additive has been demonstrated to slightly decrease the catalytic performance of the commercial catalysts, especially for the diesel oxidation and SCR ones. The chemical-physical analyses did not detect any interaction between the catalysts and nano-additives or any decrease in the specific surface areas of the catalysts.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Nano-Sized Additive Synthesis for Lubricant Oils and Compatibility Tests with After-Treatment Catalysts


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Fino, Debora (Autor:in) / Deorsola, Fabio (Autor:in) / Russo, Nunzio (Autor:in) / Bensaid, Samir (Autor:in)

    Kongress:

    10th International Conference on Engines & Vehicles ; 2011



    Erscheinungsdatum :

    2011-09-11




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    The fuel additive/lubricant interactions: compatibility assessments in field studies and laboratory tests

    Thiel,C.Y. / Hayden,T.E. / Texaco Additives International,US | Kraftfahrwesen | 2001



    Rubber and Lubricant Compatibility

    Berens, A. S. | SAE Technical Papers | 1974


    HFC-134a Lubricant Compatibility

    SAE Technical Papers | 1992


    Lubricant additive technology

    British Library Online Contents | 1997