Galvannealed steel sheets containing 10wt%Fe in coated layer were prepared in various galvannealing temperature and cooling rate. Powdering resistances were evaluated by a draw bead test. X-ray diffraction examination revealed an attribution of the coating structure to powdering resistance.Higher galvannealing temperature(500∼550°C) deteriorates powdering resistance, but slower cooling from higher temperature improves it. At low galvannealing temperature(440°C), powdering resistance is rather good independent of cooling rate. Г1-phase(Fe5Zn21) is formed along the interface between coating and steel when samples are galvannealed at lower temperature(≦500°C) or cooled at slower cooling rate from higher galvannealing temperature. The results suggest that the increase of Г1 ratio [Г1/(Г+Г1)] in the coating is inclined to improve powdering resistance.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Coating Structure on Powdering Resistance of Galvannealed Steel Sheet


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Zhang, Liwei (Autor:in) / Sakurai, Michitaka (Autor:in) / Kondo, Takaaki (Autor:in) / Tajiri, Yasuhisa (Autor:in)

    Kongress:

    International Congress & Exposition ; 1992



    Erscheinungsdatum :

    1992-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Effect of coating structure on powdering resistance of galvannealed steel sheet

    Sakurai,M. / Zhang,L. / Tajiri,Y. Kondo,T. et al. | Kraftfahrwesen | 1992


    Effect of Post Heating on Powdering Resistance of Galvannealed Steel Sheet

    Sakurai, Michitaka / Shimada, Soichi / Adaniya, Takeshi et al. | SAE Technical Papers | 1990


    Effect of post heating on powdering resistance of galvannealed steel sheet

    Tajiri,Y. / Shimada,S. / Sakurai,M. et al. | Kraftfahrwesen | 1990


    Influence of strain state on powdering of galvannealed sheet steel

    Rangarajan,V. / Jagannathan,V. / Raghavan,K.S. et al. | Kraftfahrwesen | 1996


    Influence of Strain State on Powdering of Galvannealed Sheet Steel

    Rangarajan, V. / Jagannathan, V. / Raghavan, K. S. et al. | British Library Conference Proceedings | 1996