A study for improving the resistance to fretting corrosion of SCr 420 pinion gear was conducted. Fretting is the damage to contacting surfaces experiencing slight relative reciprocating sliding motion of low amplitude. Fretting corrosion is the fretting damage to unlubricated contacting surfaces accompanied by corrosion, mostly oxidation that occurs if the fretting occurs in air. Two kinds of conventional heat treatment and a newly designed one suggested for improving the resistance to the fretting corrosion of pinion gear were compared each other to find out what is the main factor for generating fretting corrosion phenomenon. Increased carbon potential at both the heating and diffusing zone and reduced time of tempering was found out to be a solution for improving the resistance to fretting corrosion of forged and heat treated gear steel. On the contrary, modified carbo-nitriding using ammonia gas has been getting worse the fretting corrosion problem.
A Study for Improving the Resistance to Fretting Corrosion of SCr 420 Gear Steel
Sae Technical Papers
Asia Pacific Automotive Engineering Conference ; 2007
2007-08-05
Aufsatz (Konferenz)
Englisch
A study for improving the resistance to fretting corrosion of SCr 420 gear steel
Kraftfahrwesen | 2007
|Fretting corrosion and fretting fatigue in the transport industrie
Tema Archiv | 1977
|REVIEW OF FRETTING CORROSION THEORY
SAE Technical Papers | 1954
|Corrosion and Fretting Effects on Fatigue
SAE Technical Papers | 1982
|Corrosion and fretting effects on fatigue
Kraftfahrwesen | 1982
|