High temperature modulus of rupture (MOR) data, published previously, show that the ceramic catalyst supports get stronger with temperature due to the absence of water vapor and closure of microcracks which would otherwise act as stress concentrators [1, 2 and 3]*. The increased MOR value is partially responsible for the excellent durability of ceramic catalyst supports at high temperature. In this paper, we will present the compressive strength data of ceramic substrates at high temperature, namely the crush strength along B-axis and biaxial compressive strength of the whole substrate. Since the honeycomb strength is directly related to that of the individual cell wall, the compressive strength should also increase with temperature similar to the modulus of rupture. Accordingly, the ceramic substrates are capable of supporting higher mounting pressures exerted by the intumescent mat at high temperature [4]. The increased biaxial compressive strength at high temperature permits a robust mounting system for circular substrates. Similarly, the higher crush strength along B-axis ensures a robust mounting system for oval substrates. These data help ensure the long-term durability of ceramic catalyst supports over a wide temperature range representative of operating conditions.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    High Temperature Compressive Strength of Extruded Cordierite Ceramic Substrates


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Reddy, K. P. (Autor:in) / Gulati, Suresh T. (Autor:in)

    Kongress:

    International Congress & Exposition ; 1995



    Erscheinungsdatum :

    1995-02-01




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    High temperature compressive strength of extruded cordierite ceramic substrates

    Gulati,S.T. / Reddy,K.P. / Corning Glass,US | Kraftfahrwesen | 1995


    Isostatic strength of extruded cordierite ceramic substrates

    Gulati,S.T. / Widjaja,S. / Xu,W. et al. | Kraftfahrwesen | 2004


    Isostatic Strength of Extruded Cordierite Ceramic Substrates

    Gulati, S. T. / Widjaja, S. / Xu, W. et al. | British Library Conference Proceedings | 2004


    Isostatic Strength of Extruded Cordierite Ceramic Substrates

    Treacy, D. R. / Yorio, J. A. / Widjaja, S. et al. | SAE Technical Papers | 2004


    2004-01-1135 Isostatic Strength of Extruded Cordierite Ceramic Substrates

    Gulati, S. T. / Widjaja, S. / Xu, W. et al. | British Library Conference Proceedings | 2004