Carbon fiber sheet molding compound (SMC) is an attractive material for automotive lightweighting applications, but several issues present themselves when adapting a process developed for glass fiber composites to instead use carbon fibers. SMC is a discontinuous fiber material, so individual carbon fiber tows must be chopped into uniform rovings before being compounded with the resin matrix. Rotary chopping is one such method for producing rovings, but high wear rates are seen when cutting carbon fibers. Experiments were performed to investigate the wear progression of cutting blades during rotary carbon fiber chopping. A small rotary chopper with a polyurethane (PU) backing and thin, hardened steel blades was used to perform extended wear tests (120,000 chops, or until failure to reliably chop tows) to simulate the lifespan of blades during composite material production. Backings of different hardness were tested, as well as several intentionally profiled backings with grooves machined into their surfaces. The key measure of blade wear was obtained by examining the side face of the blade under a microscope and measuring the maximum depth of its crescent-shaped wear pattern while butted against a flat datum edge. Cutting-edge rounding progression was also examined by comparison of abraded regions, and parallels between this work and previous observations are drawn. Blade wear rates were found to decrease as backing hardness increased, as harder backings were more prone to forming grooves naturally during fiber chopping. Intentionally grooved backing rolls were seen to have little effect on wear rates as compared to plain backings, also due to the tendency of backings to form grooves naturally.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Effect of Backing Profile on Cutting Blade Wear during High-Volume Production of Carbon Fiber-Reinforced Composites


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:

    Kongress:

    WCX World Congress Experience ; 2018



    Erscheinungsdatum :

    2018-04-03


    Format / Umfang :

    8 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    BACKING FOR WIPER BLADE, WIPER BLADE, AND WIPER DEVICE

    MATSUMOTO HIROSHI | Europäisches Patentamt | 2016

    Freier Zugriff

    Fiber Reinforced Polymer Blade

    LIEU BRENNAN / GUO AARON | Europäisches Patentamt | 2024

    Freier Zugriff

    Fabrication and Wear Characteristics Basalt Fiber Reinforced Polypropylene Matrix Composites

    R, Arun / M, Krishnaraj / T, Thirugnana Sambandha et al. | SAE Technical Papers | 2019


    High-Rate Fabrication Methods for Carbon Fiber-Reinforced Composites

    Fanter, D. L. / Strandburg, D. B. / Dry, A. C. et al. | British Library Conference Proceedings | 1996


    On effect of shape of blade section on efficiency of backing marine propellers

    Van Aken, J.A. / Tasseron, K. | Engineering Index Backfile | 1955