The use of natural fibers in composite materials of plant origin involves environmental, social and economic factors that must be met. Moreover, there is a shortage of progressive energy and mineral resources in general. Leading the search for renewable raw materials and low cost, which has been the factor of significant importance in directing research involving the use of natural fibers in composites. The paper presents polyester matrix composites reinforced by short sisal fibers, randomly arranged in the mold without using technological stages of production. The resin used was polyester terephthalic pre-accelerated in relation curing agent/resin of 0,33% by volume. The sisal fibers were acquired in the local market of Belem of Para. The fibers were manually cut in lengths of 5, 10 and 15 mm, untreated and at room temperature. The fibers were characterized mechanical, physically and microstructurally. The composites were made by molding by hand without pressure and room temperature by varying the length of the fibers and different proportions between the constituents in the relationship fiber length/mass fraction (5 mm/5,41%), (10 mm/4,87%) and (15 mm/3,90%). The composites were evaluated in tensile test and evaluation of the fractured surface by scanning electron microscopy (SEM) to determine the dominant failure mechanisms for each series of composites produced. The sisal fibers showed strength (453,62 MPa) and density (1,42 g/cm₃). For composite sisal 5 mm tensile strength was 16,98 MPa, for the composite sisal 10 mm tensile strength was 22,78 MPa and the composites sisal 15 mm tensile strength was 27,05 MPa. For composite sisal greater resistance to mechanical failure mechanisms dominating was the breaking of the fibers, sisal the composites of lower resistance to mechanical failure mechanisms were predominant the pull out (tearing of the fibers) and the detachment of the fiber matrix.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Characterization of Composite with Polyester Matrix and Natural Fiber (Agave Sisalana)


    Weitere Titelangaben:

    Sae Technical Papers



    Kongress:

    21st SAE Brasil International Congress and Exhibition ; 2012



    Erscheinungsdatum :

    2012-10-02




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Enzymatic surface modification of sisal fibers (Agave Sisalana) by Penicillium echinulatum cellulases

    González, J. T. / Dillon, A. J. / Pérez-Pérez, A. R. et al. | British Library Online Contents | 2015


    LAMINATE OF COMPOSITES OF NATURAL FIBER (saotome banana) AND POLYESTER MATRIX

    El Banna, W.R. / Dos Santos, I.P. / Fujiyama, R.T. et al. | British Library Conference Proceedings | 2012


    Mechanical and machining characterization of Agave Americana. pineapple and its hybrid fiber composites

    Babu, G. Dilli / Bhavan, Garikapati / Babu, K. Sivaji | TIBKAT | 2021


    Laminate of Composites of Natural Fiber (São-Tomé banana) and Polyester Matrix

    dos Santos, Izael Pinho / Fujiyama, Roberto Tetsuo / El Banna, Wassim Raja | SAE Technical Papers | 2012


    Aging in Natural Water of Composite of Polyester Resin and Sisal Fiber

    Filho, Carlindo Lins Pereira / Silva, Douglas Santos / Teixeira, Felipe Pinheiro et al. | SAE Technical Papers | 2014