The fatigue behavior of five microalloyed steels, processed with hardnesses between 25-28 HRC containing microstructures ranging from precipitation-hardened ferrite-pearlite to bainite, were evaluated in both low cycle (strain controlled) and high cycle (stress controlled fatigue. The vanadium-bearing steels included, 15R30V, 1522 MoVTi, 1522 MoVTiS, 1534 MoVTi, and 1534 MoVTiSi. Conventional quench and tempered 4140 steel was used as a reference.Low cycle fatigue (LCF) data for all steels were similar. Subtle microstructural-dependent differences in the high-strain amplitude region of the LCF curves were attributed to the effects of retained austenite, present in some of the non-traditional bainitic steels. In high cycle fatigue, all steels exhibited similar properties, except for the ferrite-pearlite steel (15R30V) which exhibited the lowest endurance limit, an observation which was attributed to crack nucleation in coarse-grained ferrite.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fatigue of Microalloyed Bar Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE 2000 World Congress ; 2000



    Erscheinungsdatum :

    2000-03-06




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    Fatigue of Microalloyed Bar Steels

    Johnson, J. A. / Krauss, G. / Matlock, D. K. et al. | British Library Conference Proceedings | 2000


    Fatigue of microalloyed bar steels

    Johnson,J.A. / Krauss,G. / Matlock,D.K. et al. | Kraftfahrwesen | 2000


    Evalution of fatigue properties of microalloyed forging steels

    Hui, Weijun / Zha, Xiaoqin / Zhang, Yingjian et al. | Tema Archiv | 2006


    Microalloyed high-strength steels

    Olsson, Kennet / Gladh, Magnus / Hedi, Jan-Erik et al. | Tema Archiv | 2006


    Microalloyed steels for automobile components

    Matsushima, Y. / Hasegawa, T. | Tema Archiv | 1997