Abstract The maximum principal stresses, von Mises effective stresses and principal facet stresses at the time of creep rupture were compared in uniaxial, biaxial, and triaxial stress states for AZ31 magnesium alloy. The creep rupture of this alloy was experimentally controlled by cavitation, which was the result of a low damage tolerance, λ. Creep deformation could be correlated with the von Mises effective stress parameter. The failure-mechanism control parameter governing the stress state coincided with the experimental results of the rupture of the materials under multiaxial stress states. Finally, the theoretical prediction based on constrained cavity growth and continuous nucleation agreed with the experimental rupture data to within a factor of three.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Multiaxial stress creep rupture mechanisms of AZ31 magnesium alloy


    Beteiligte:
    Kim, S. H. (Autor:in) / Kim, H. K. (Autor:in)


    Erscheinungsdatum :

    2009




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch


    Klassifikation :

    BKL:    55.20$jStraßenfahrzeugtechnik / 55.20 Straßenfahrzeugtechnik



    Multiaxial stress creep rupture mechanisms of AZ31 magnesium alloy

    Kim, S. H. / Kim, H. K. | Springer Verlag | 2009


    Multiaxial stress creep rupture mechanisms of AZ31 magnesium alloy

    Kim, S. H. / Kim, H. K. | British Library Online Contents | 2009


    Ion Implanted AZ31 Magnesium Alloy

    Wu, G. S. / Zeng, X. Q. / Yao, S. S. et al. | British Library Conference Proceedings | 2007


    Rolling of AZ31 Magnesium Alloy Thin Strip

    Jiang, B. / Wang, J. / Ding, P. D. et al. | British Library Conference Proceedings | 2007


    Warm Hydroforming of Magnesium Alloy AZ31 Sheets

    Zhang, S. / Ren, L. M. / Zhou, L. X. et al. | British Library Conference Proceedings | 2007