The debonding distress in asphalt pavement structures is a critical problem that affects the performance of asphalt concrete pavements. It occurs at the layer interface due to the poor bond quality between adjacent asphalt concrete layers and/or when stresses at the layer interface exceed the strengths of the material at the interface. The debonding of the adjacent layers, especially the top surface layer of an asphalt pavement, is a contributing factor to the premature cracking of pavements. Hence, the debonding distress can lead to a reduction in the life of the pavement. This paper presents an analytical and experimental framework to evaluate the potential for debonding at the layer interface of asphalt concrete pavements. Computational analysis was performed to determine the critical stress and strain states in layered asphalt pavements under moving vehicle loads using the Layered ViscoElastic pavement analysis for Critical Distresses (LVECD) computer program developed at North Carolina State University. This computational analysis enables a greater understanding of the critical stress that is involved in debonding and the ways that such stress is affected by pavement design parameters and environmental conditions. In addition, a prediction model was developed that can determine the shear bond strength at the interface of asphalt concrete layers with different tack coat materials at various temperatures, loading rates and normal confining stresses. The systematic and mechanistic framework developed in this study employs the maximum shear ratio concept as a shear failure criterion and provides a tool to evaluate the effects of various loading, environmental and pavement factors on the debonding potential of asphalt pavements. The overall advantages of the mechanistic framework and approach using the LVECD analysis tool will help lead to better understanding of the debonding mechanism, proper selection of the tack coats, and economic benefit in highway pavement maintenance and rehabilitation costs.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A mechanistic approach to evaluate the potential of the debonding distress in asphalt pavements




    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    56.24 Straßenbau / 56.24




    Analysis of Thermal Fatigue Distress of Asphalt Concrete Pavements

    Jackson, N. Mike / Vinson, Ted S. | Transportation Research Record | 2019


    Identification of Potential Location and Extent of Localized Interface Debonding in the Wheelpath of Asphalt Pavements

    Hernando, David / Waisome, Jeremy A. M. / Zou, Jian et al. | Transportation Research Record | 2018


    Analysis of Thermal Fatigue Distress of Asphalt Concrete Pavements

    Jackson, N. / Vinson, Ted | Transportation Research Record | 1996


    Mechanistic evaluation of fatigue cracking in asphalt pavements

    Norouzi, Amirhossein | Online Contents | 2017