Fatigue cracking is one of the major types of distress in asphalt mixtures and is caused by the accumulation of damage in pavement sections under repeated load applications. The fatigue endurance limit (EL) concept assumes a specific strain level, below which the damage in hot mix asphalt (HMA) is not cumulative. In other words, if the asphalt layer depth is controlled in a way that keeps the critical HMA flexural strain level below the EL, the fatigue life of the mixture can be extended significantly. This paper uses two common failure criteria, the traditional beam fatigue criterion and the simplified viscoelastic continuum damage model energy-based failure criterion (the so-called G R method), to evaluate the effect of different parameters, such as reclaimed asphalt pavement (RAP) content, binder content, binder modification and warm mix asphalt (WMA) additives, on the EL value. In addition, both failure criteria are employed to investigate the impacts of these parameters in terms of the fatigue life of the study mixtures. According to the findings, unlike an increase in RAP content, which has a negative effect on the mixtures' fatigue resistance, a higher binder content and/or binder modification can significantly increase the EL value and extend the fatigue life as was proved before by other researchers, whereas WMA additives do not significantly affect the mixtures' fatigue behaviour. A comparison of the model simulation results with the field observations indicates that the G R method predicts the field performance more accurately than the traditional method.
Fatigue life and endurance limit prediction of asphalt mixtures using energy-based failure criterion
2017
Aufsatz (Zeitschrift)
Englisch
Viscoelasticity , Mathematical models , Parameter modification , fatigue failure criterion , Damage assessment , Cracking (fracturing) , endurance limit , Fatigue failure , Computer simulation , Additives , Damage accumulation , Fatigue cracking , Fatigue limit , field observations , Crack propagation , Studies , Criteria , Asphalt pavements , Asphalt pavement , Fatigue life , fatigue life , Energy use , Fatigue strength , Fracture mechanics
Fatigue life and endurance limit prediction of asphalt mixtures using energy-based failure criterion
Online Contents | 2016
|PART 2 -- ASPHALT MIXTURES 2000 - Energy-Derived, Damage-Based Failure Criterion for Fatigue Testing
Online Contents | 2000
|Impact of asphalt concrete fatigue endurance limit definition on pavement performance prediction
Online Contents | 2017
|Impact of asphalt concrete fatigue endurance limit definition on pavement performance prediction
Online Contents | 2016
|Laboratory Validation of Healing-Based Fatigue Endurance Limit for Hot-Mix Asphalt
Online Contents | 2013
|