Epoxy asphalt curing system was prepared by sebacic acid compound with methyl-tetrahydrophthalic anhydride (MeTHPA) or Tung oil anhydride (TOA). Tensile strength, penetration, differential scanning calorimetry, dynamic mechanical thermal analysis, torn section microscopy photographs and scanning electron microscope analysis were utilised to investigate the mechanical properties, thermodynamic behaviour and micro-structure of epoxy asphalt curing systems under different curing agents. The results showed that in the presence of compound curing agent, the tensile strength and surface hardness of the epoxy asphalt curing system effectively improved, the induction period of the curing reaction decreased, the curing reaction mechanism turned to one-step reaction from two-step reaction, the Tg of asphalt phase and epoxy phase could simultaneously increase, and high-temperature damping performance also improved, but the particle size of asphalt dispersed in epoxy resin becomes uneven, while the curing system becomes semi-brittle from toughness. Compared to TOA, the effects of MeTHPA on such performance were more obvious.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren




    Exploration of Curing Characteristics of Epoxy-Modified Asphalt

    Dongre, Raj / Andriescu, Adrian / Elwardany, Michael et al. | Transportation Research Record | 2023