Polycrystalline CdS/CdTe thin‐film solar cells in the superstrate configuration have been studied by spectroscopic ellipsometry (SE) using glass side illumination. In this measurement method, the first reflection from the ambient/glass interface is rejected, whereas the second reflection from the glass/film‐stack interface is collected; higher order reflections are also rejected. The SE analysis incorporates parameterized dielectric functions ε for solar cell component materials obtained by in situ and variable‐angle SE. In the SE analysis of the complete cells, a step‐wise procedure ranks the fitting parameters, including thicknesses and those defining the spectra in ε , according to their ability to reduce the root‐mean‐square deviation between the simulated and measured SE spectra. The best fit thicknesses from this analysis are found to be consistent with electron microscopy. Based on the SE results, the solar cell quantum efficiency (QE) can be simulated without any free parameters, and comparisons with measured QE enable optical model refinements as well as identification of optical and electronic losses. These capabilities have wide applications in photovoltaic module mapping and in‐line monitoring. Copyright © 2016 John Wiley & Sons, Ltd. Polycrystalline CdS/CdTe thin‐film solar cells in the superstrate configuration have been studied by spectroscopic ellipsometry (SE) using glass side illumination, and the results have been compared with electron microscopy. The SE results can be combined to simulate the solar cell quantum efficiency (QE) without free parameters, and comparisons with QE measurements enable identification of losses. The capabilities have wide applications in photovoltaic module mapping and in‐line monitoring.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Through‐the‐glass spectroscopic ellipsometry for analysis of CdTe thin‐film solar cells in the superstrate configuration



    Erschienen in:

    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    53.36 Energiedirektumwandler, elektrische Energiespeicher