We present the effects of an In‐Se surface treatment of Cu‐rich ([Cu]/[In] > 1) CuInSe 2 absorbers in order to utilize the superior transport properties of Cu‐rich absorbers for high‐efficiency solar cells. A Cu‐poor surface was successfully formed on a Cu‐rich absorber by co‐evaporation of indium and selenium under appropriate conditions. The aim is to suppress the interface recombination, which is generally observed at the interface between CdS and Cu‐rich CuInSe 2 . A surface‐treated device achieved an efficiency of 13.1%, improved from 9.5% obtained with an untreated Cu‐rich device. The open‐circuit voltage of In–Se treated devices reach the same level as devices made from Cu‐poor absorbers grown by a three‐stage process. By comparing the results of the experiments and simulations, it is shown that the role of the Cu‐poor surface on Cu‐rich absorbers is to prevent interface recombination, mainly due to a lower doping level of the Cu‐poor surface layer than in the Cu‐rich CuInSe 2 . Thus, it becomes possible to uncouple the interface from the bulk properties in Cu‐rich solar cells. Copyright © 2014 John Wiley & Sons, Ltd. The effects of an In–Se surface treatment of Cu‐rich ([Cu]/[In] > 1) CuInSe 2 absorbers were presented. An In–Se surface treatment does improve the performance of “Cu‐rich” solar cells by increasing the open‐circuit voltage and reducing interface recombination, which is known as the main limitation of Cu‐rich devices. According to the electrical modeling, the role of the Cu‐poor surface is to prevent the interface recombination simply by reducing the doping level within the space charge region.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Cu‐rich CuInSe2 solar cells with a Cu‐poor surface



    Erschienen in:

    Erscheinungsdatum :

    2015




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch



    Klassifikation :

    BKL:    53.36 Energiedirektumwandler, elektrische Energiespeicher



    Bulk p-CuInSe2 photo-electrochemical solar cells

    Djellal, L. | Online Contents | 2008


    Properties of ZnO-CdS-CuInSe2 solar cells with improved performance

    Abushama, Jehad A.M. | Online Contents | 2004


    The electron affinity difference in CdS-CuInSe2 solar cells

    Al Kuhaimi, Siham A. | Online Contents | 1998



    Lightweight (AlGaAs)GaAs/CuInSe2 tandem junction solar cells for space applications

    Kim, N.P. / Stanbery, B.J. / Burgess, R.M. et al. | Tema Archiv | 1989