Oxidation and embrittlement are concerns in use of titanium foils for shielding advanced space transportation system vehicles during Earth reentry. Ti-6Al-4V in 0.003 in. and 0.035 in. thicknesses were exposed to multiple cycles of simulated space transportation system ascent/reentry conditions at temperatures ranging from 1000 F to 1200 F. Residual mechanical tests and metallurgical analyses were made on the specimens after exposure. Results show that tensile elongation is the mechanical property most affected by the reentry environment. Results are presented to show a comparison of residual properties of foil specimens from static oxidation exposure and cyclic oxidation exposure.
Residual mechanical properties of Ti-6Al-4V after simulated Space Shuttle reentry
Ann. Meeting of TMS-AIME ; 1984 ; Los Angeles, CA, United States
1983-08-01