Space Shuttle Discovery's last mission, STS-133, was scheduled to launch on November 5, 2010. Just hours before liftoff, a hydrogen leak at an umbilical connection scrubbed the launch attempt. After the scrub, further inspection revealed a large crack in the foam insulation covering the External Tank, ET-137. Video replay of the launch attempt confirmed the crack first appeared as cryogenic propellants were being loaded into the ET. When the cracked foam was removed, technicians found the underlying stringer had two 9-inch-long cracks. Further inspection revealed a total of 5 of the 108 ET stringers had cracked. NASA and Lockheed Martin immediately launched an aggressive campaign to understand the cracks and repair the stringers in ET-137, targeting February 2011 as the new launch date for STS-133. Responsibilities for the various aspects of the investigation were widely distributed among NASA centers and organizations. This paper will focus on lab testing at Marshall Space Flight Center (MSFC) in Huntsville, Alabama that was intended to replicate the stringer failure and gauge the effect of proposed countermeasures.
Stringer Bending Test Helps Diagnose and Prevent Cracks in the Space Shuttle's External Tank
2012
8 pages
Report
Keine Angabe
Englisch
Manned Spacecraft , Nondestructive Testing , Fuel & Propellant Tanks , Stringers , Bend tests , Discovery(Orbiter) , External tanks , Cracking(Fracturing) , Hydrogen , Failure analysis , Oxygen-hydrocarbon rocket engines , Leakage , Bending , Cracks , Space shuttles , Structural failure , Finite element method , Deflection , Loads(Forces) , Cryogenic rocket propellants , Umbilical connectors
Stringer Bending Test Helps Diagnose and Prevent Cracks in the Space Shuttle's External Tank
British Library Conference Proceedings | 2012
|System for Orbital Recovery of Space Shuttle's External Tank
Online Contents | 1994
|The Space Shuttle's testing gauntlet
NTRS | 1976
|