Wheel, which works under serious condition on the trainset, is the key component affecting the service safety of trainset. Besides manufacturing defect, tread defect and inner crack of wheel are the common defects generated during service. Of which the rim fatigue crack is the most common one. Failure analysis indicates that the inclusion has great influence on the initiation of fatigue crack in rim. By analysis the cause of rim crack and its rule of propagation, the paper summarize the wheel failure mode in complex service condition (high speed, heavy load) and put forward the resolution strategy.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Understanding and discussion on fatigue crack in wheel rims


    Beteiligte:
    Zhang, Bin (Autor:in) / Zhang, Peng-Pm (Autor:in) / Zhang, Guan-Zhen (Autor:in) / Wang, Xu-Dong (Autor:in)


    Erscheinungsdatum :

    2016-11-01


    Format / Umfang :

    1475559 byte




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Operational stresses of wheel rims

    Svenson, O. | Engineering Index Backfile | 1965


    Wheel rim manufacturing method and wheel rims

    GONG BAOGANG | Europäisches Patentamt | 2015

    Freier Zugriff

    Evolution in chilled wheel rims

    Engineering Index Backfile | 1948



    Vision system rolls mixed wheel rims

    Masi, C.G. | Tema Archiv | 2003