Broadband near-infrared emission from nickel in zinc-alumino-silicate glass was observed at room temperature. The center and width of the emission band were /spl sim/1400 nm and >300 nm respectively. The emission lifetime was >200 /spl mu/sec even at room temperature.
Room temperature broadband near-infrared emission from nickel in zinc-alumino-silicate glass