PROBLEM TO BE SOLVED: To enhance vulcanized rubber properties of a rubber composition obtained from the rubber wet master batch by inhibiting cutting a molecular chain of a rubber polymer by heat generated by a shear force while enhancing dispersion degree of a filler with adding shear force to a filler-containing rubber coagulum.SOLUTION: There is used a manufacturing method of a rubber master batch obtained by using a filler, a dispersion solvent and a rubber latex solution as raw materials and having a solidification process, a dehydration process of adding shear force till moisture content of the coagulum becomes 10% or less and dehydrating to manufacture the rubber master batch, a cooling process of cooling the rubber wet master batch and a drying process of drying the cooled rubber wet master batch.SELECTED DRAWING: None

    【課題】本願発明は、充填剤含有ゴム凝固物にせん断力を加えて更に充填剤の分散度を高めつつ、せん断力により発生する熱がゴムポリマーの分子鎖を切断することを防止し、前記ゴムウェットマスターバッチから得られるゴム組成物の加硫ゴム特性を向上させることを目的とする。【解決手段】本発明では、充填剤、分散溶媒及びゴムラテックス溶液を原料として得られるゴムウェットマスターバッチの製造方法であって、凝固工程と、凝固物を含水率10%以下になるまでせん断力を加えることにより脱水してゴムウェットマスターバッチを製造する脱水工程と、前記ゴムウェットマスターバッチを冷却する冷却工程と、冷却されたゴムウェットマスターバッチを乾燥する乾燥工程とを有するゴムウェットマスターバッチの製造方法を用いる。【選択図】なし


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    MANUFACTURING METHOD OF RUBBER WET MASTER BATCH, RUBBER COMPOSITION AND MEMBER FOR TIRE


    Weitere Titelangaben:

    ゴムウェットマスターバッチの製造方法、ゴム組成物及びタイヤ用部材


    Beteiligte:
    NAKANISHI KOTA (Autor:in)

    Erscheinungsdatum :

    2016-10-06


    Medientyp :

    Patent


    Format :

    Elektronische Ressource


    Sprache :

    Japanisch


    Klassifikation :

    IPC:    C08J Verarbeitung , WORKING-UP / B60C VEHICLE TYRES , Fahrzeugreifen




    Process for producing rubber wet master batch, rubber composition and tire

    NAKAYAMA ATSUSHI / IZUCHI MASAAKI / NISHIURA FUMITERU et al. | Europäisches Patentamt | 2017

    Freier Zugriff