The purpose of this study was to optimize the surface roughness (Ra), delamination damage at the hole entrance (FdT) and at the hole exit (FdB) and kerf angle (K) in the drilling of aramid fiber-reinforced polymer (AFRP) composite material using abrasive water jet (AWJ) machining.

    Design/methodology/approach

    The AFRP composite was produced by the vacuum infusion method. The drilling experiments were performed on an AWJ machine using a three-axis computerized numerical control system. Machine processing parameters were determined as water pressure (2,000, 3,000 and 4,000 bar), stand-off distance (2, 4 and 6 mm) and traverse feed rate (150, 250 and 350 mm/min). Optimization of processing parameters in the drilling experiments was carried out according to the Taguchi L27 (33) orthogonal array. In addition, gray relational analysis (GRA) was used to analyze the complex uncertainty affecting the results.

    Findings

    Results of the drilling operations demonstrated that water pressure (P) was the most effective parameter, with 65.3%, 65.2%, 49.8% and 52.1% contribution rates for Ra, FdT, FdB and K, respectively.

    Practical implications

    Reliable results have been obtained with Taguchi-based GRA while drilling AFRP composite material using AWJ. Significant results have been achieved to increase the hole quality in the drilling of AFRP composite material.

    Originality/value

    The new approach is to present more detailed analysis by using Taguchi method and multi-decision Taguchi-based gray relation analysis in AFRP composite material drilling using AWJ. Thus, time and experiment costs are saved.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Investigation of effect of abrasive water jet (AWJ) machining parameters on aramid fiber-reinforced polymer (AFRP) composite materials


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2021-06-04


    Format / Umfang :

    1 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Adsorbed Aramid Nanofiber Interphase for Enhanced Aramid Fiber Reinforced Composites

    Nasser, Jalal / Lin, Jiajun / Steinke, Kelsey et al. | AIAA | 2019


    Aramid-reinforced tyres

    Tema Archiv | 2009


    Aramid - reinforced thermoplastics

    Theberge,J.E. / Crosby,J. / Hutschins,M. | Kraftfahrwesen | 1985