Clad 2024-T3 and 7075-T6 sheet specimens were loaded at three different load amplitudes and three different mean loads. It turned out that the mean stress had an important influence on the crack propagation rate. The crack growth rate in the 7075 specimens was three to four times as large as in the 2024 specimens.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The Influence of the Mean Stress on the Propagation of Fatigue Cracks in Light Alloy Sheet


    Untertitel :

    An investigation into the effect of reducing stress levels on the rate of crack propagation


    Beteiligte:
    Broek, D. (Autor:in) / Schijve, J. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1967-03-01


    Format / Umfang :

    9 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Propagation of fatigue cracks in wide unstiffened aluminium alloy sheets

    Raithby, K. D. / Bebb, Marie E. / Aeronautical Research Council | TIBKAT | 1963


    Influence of Mean Stress on Contact Wire Fatigue

    Yamashita, C. / Sugahara, A. | British Library Online Contents | 2006


    On propagation of short rolling contact fatigue cracks

    Ringsberg, J.W. / Bergkvist, A. | Tema Archiv | 2003


    ANALYSIS OF FATIGUE CRACKS PROPAGATION IN COMPLEX STRUCTURES

    Kaniowski, J. / Szala, J. | British Library Online Contents | 2003