AbstractThe ablation spot area and impulse characteristics of various polymers were experimentally investigated against burst irradiation of Nd: YLF laser pulses with a pulse repetition frequency of 1kHz, wavelength of 1047nm, temporal pulse width of 10ns, and single-pulse fluence of 6.1J/cm2 to 17.1J/cm2. The dependences of ablation area on the pulse energy from 0.72 to 7.48mJ and the number of pulses from 10 pulses to 1000 pulses were investigated. In order to characterize their impulse performance as a function of fluence, which should not depend on ablation material, an effective ablation spot area was defined as that obtained against aluminum, 1050A, as the reference material. An impulse that resulted from a single burst of 200 pulses was measured with a torsion-type impulse stand. Various impulse dependences on the fluence, which were not readily predicted from the optical properties of the material without ablation, were obtained. By fitting the experimentally measured impulse performance to Phipps and Sinko's model in the vapor regime, the effective absorption coefficient with laser ablation was evaluated, thereby resulting in three to six orders of magnitude larger than that without ablation. Among the polymers examined using polytetrafluoroethylene (PTFE) as the best volume absorbers, the highest momentum coupling coefficient of 66 μNs/J was obtained with an effective absorption coefficient more than six times smaller than that of the other polymers.

    HighlightsThe burnt surface on aluminum shows excellent reproducibility of laser spot area.Laser ablation impulse performance of polymers exhibited strong material dependence.The momentum coupling coefficient, Cm, of polymers exceeded the maximum of aluminum.An effective absorption coefficient during ablation is dominant for Cm.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Ablation spot area and impulse characteristics of polymers induced by burst irradiation of 1µm laser pulses


    Beteiligte:
    Tsuruta, Hisashi (Autor:in) / Dondelewski, Oskar (Autor:in) / Katagiri, Yusuke (Autor:in) / Wang, Bin (Autor:in) / Sasoh, Akihiro (Autor:in)

    Erschienen in:

    Acta Astronautica ; 136 ; 46-54


    Erscheinungsdatum :

    2017-03-08


    Format / Umfang :

    9 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Ablation Impulse Characteristics by Laser Pulse Irradiation

    Matsuda, Atsushi / Sakai, Takeharu / Sasoh, Akihiro | AIAA | 2009


    Ablation Impulse Characteristics by Laser Pulse Irradiation

    Matsuda, A. / Sakai, T. / Sasoh, A. et al. | British Library Conference Proceedings | 2009


    Measurement of ablation impulse and direction with oblique laser-pulse irradiation

    Nakamura, Yusuke / Moriyama, Daichi / Isomura, Atsushi et al. | Elsevier | 2023



    Study of laser ablation induced impulse for laser space debris removal

    Tsuno, Katsuhiko / Wada, Satoshi / Ogawa, Takayo et al. | British Library Conference Proceedings | 2023