AbstractTo investigate the silicon contamination effects on tribology in low earth orbit, diamond-like carbon (DLC) film, Ti plate, and single crystal MoS2 were exposed to dimethylsilicone (PDMS) in an ultra high vacuum (UHV) facility equipped with a tribometer and X-ray photoelectron spectroscopy (XPS). In-situ tribological tests and surface analyses were conducted without ambient air exposure. The PDMS exposure led to their adsorptions on the DLC and Ti sample surfaces and did not affect the friction property of the DLC samples. The friction of the Ti sample became low due to the PDMS adsorption. A little of PDMS were adsorbed on the MoS2 sample. The hyperthermal atomic oxygen (AO) irradiation broke C–O and C–Si bonds included in PDMS that adsorbed on the DLC and Ti surfaces. The low friction due to the PDMS adsorption for the Ti sample disappeared due to the hyperthermal AO irradiation.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Influence of silicon contamination on tribology in low earth orbit


    Beteiligte:

    Erschienen in:

    Acta Astronautica ; 66 , 9-10 ; 1320-1324


    Erscheinungsdatum :

    2009-11-08


    Format / Umfang :

    5 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch






    Return flux contamination of an outgassing spacecraft in low earth orbit

    JUSTIZ, CHARLES / DALTON, CHARLES / IGNATIEV, ALEX et al. | AIAA | 1993


    Return flux contamination of an outgassing spacecraft in low earth orbit

    Justiz, Charles R. / Dalton, Charles / Ignatiev, Alex et al. | NTRS | 1993


    Earth Orbit on-Orbit Operations in Near-Earth

    Czysz, Paul A. / Bruno, Claudio / Chudoba, Bernd | Springer Verlag | 2017