This paper reports the development of a new optical instrument capable of characterizing the aging process of enhanced first surface aluminum reflectors for concentrating solar power (CSP) application. Samples were exposed outdoors at different sites and in accelerated exposure tests. All samples exposed outdoors showed localized corrosion spots. Degradation originated from points of damage in the protective coating, but propagated underneath the protective coating. The degraded samples were analyzed with a microscope and with a newly designed space-resolved specular reflectometer (SR)2 that is capable of optically detecting and characterizing the corrosion spots. The device measures the specular reflectance at three acceptance angles and the wavelengths with spatial resolution using a digital camera’s CMOS sensor. It can be used to measure the corrosion growth rate during outdoor and accelerated exposure tests. These results will allow a correlation between the degraded mirror surface and its specular reflectance.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    A new method to characterize degradation of first surface aluminium reflectors


    Beteiligte:

    Kongress:

    2010 ; Perpignan, Frankreich



    Erscheinungsdatum :

    2010-09-21


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Degradation Of Reflectors And Dielectrics

    Bouquet, Frank L. / Cuddihy, Edward F. / Maag, Carl R., Jr. | NTRS | 1987



    Complex surface reflectors

    Valeo,FR | Kraftfahrwesen | 1988



    Folding concept for flexible surface reflectors

    Tibbalds, B. / Guest, S. / Pellegrino, S. | AIAA | 1998