Data show that susceptibility to causes of brittle fractures in ductile metal such as fatigue, stress corrosion cracking, and biaxial tension can be reduced by development and retention of residual compressive stress in vulnerable areas; methods for reducing harmful residual stresses; since welded ships are fabricated from ductile steel and fracture origins of failed ship plates are brittle in character, ship failures are suspected of developing from several causes.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Brittle structural failures with emphasis on welded ships


    Weitere Titelangaben:

    Product Eng


    Beteiligte:
    Almen, J.O. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1953


    Format / Umfang :

    12 pages


    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    Failures in welded ships

    Engineering Index Backfile | 1952


    THE INVESTIGATION OF STRUCTURAL FAILURES IN SHIPS

    Colman, J. C. / Royal Institution of Naval Architects | British Library Conference Proceedings | 2002


    Structural design of welded cargo ships

    Groeneveld, H.W. | Engineering Index Backfile | 1962


    Welded ships

    Engineering Index Backfile | 1952


    Welded ships

    Engineering Index Backfile | 1945