Partial block-dropping phenomenon was existed during the precision process of TA15 titanium alloy casting. In view of multiple means of microscopic physical characterization analysis such as OM/SEM/EDS/XRD and by considering the tensile performance results, the microstructure and mechanical properties between block-dropping area and the regular areahad been investigated. This article focused on the impact mechanism on tensile behavior that generated from the abnormal structure of block-dropping area. The results reveal that both the block-dropping area and the regular area show bi-modal microstructure, whereas the β phase concentration of the block-dropping area is far beyond the regular area and emerges as β spot. Microanalysis shows that the segregation of Fe is the major factor causing the abnormal structure and β spot, as well as the sharp plasticity decreases of alloy. The segregated Fe alters the microstructure and properties of the alloy, mainly because the saturation of Fe in α-Ti is only 0.1%, which leads to the formation of brittle TiFe eutectic phase. The increase of strength reduces the plasticity of the alloy casting, and further lead to the block-dropping during the process.
Formation of abnormal structure in ZTA15 titanium alloy casting and its impact mechanism on tensile behavior
2020
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Development of titanium alloy casting method
Tema Archiv | 1970
|Effect of microstructure on tensile deformation behavior of Ti-3Al-4.5V-5Mo titanium alloy
DOAJ | 2020
|Casting, Structural Investment, Titanium Alloy 6Al - 4V Hot Isostatically Pressed
SAE Technical Papers | 2023
Casting, Structural Investment, Titanium Alloy 6Al - 4V Hot Isostatically Pressed
SAE Technical Papers | 2018
Casting, Structural Investment, Titanium Alloy 6Al - 4V Hot Isostatically Pressed
SAE Technical Papers | 2014