The aluminum alloy surface was treated through three different processes. The bonding strength of GFRP-aluminum under hygrothermal environment with different surface treatments was tested and was arranged with the order of anodizing > silane coupling agent > sand blasting. The effects of hygrothermal environment and surface treatment on repair effects were also studied by tensile tests of GFRP and GFRP reinforced aluminum. The results show that the tensile strength, elastic modulus and break elongation of GFRP decrease after wet and heat treatments. After different surface treatments, the initial loads of repaired specimens increase with the order of anodizing > silane coupling agent > sand blasting. The bearing capacities of the specimens repaired by different surface treatments are reduced to different degrees under hygrothermal environment. For sand blasting specimen, the declining of bonding strength of the resin-aluminum is the main cause of the declining of bearing capacity, and damage mainly occurs in the interface. For the silane coupling agent and anodic specimen, damage occurs mainly in the resin-GFRP interface, the mechanical property of resin-aluminum interface is better than that of resin-GFRP.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Surface Treatment on Durability of GFRP Reinforced Aluminum Structure under Hygrothermal Environment


    Beteiligte:
    YU Zhouhui (Autor:in) / ZHAO Peizhong (Autor:in) / HU Fangyou (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Strength and durability of graphite/epoxy composites under hygrothermal conditions

    Davison, Sneha P. / Case, Scott W. | Tema Archiv | 2003


    Steel Reinforced Pultruded GFRP Vehicle Chassis Structure

    Honickman, Hart Noah / Johrendt, Jennifer / Frise, Peter | SAE Technical Papers | 2010


    Durability of GFRP composite exposed to various environmental conditions

    Kim, Hyeong-Yeol / Park, Young-Hwan / You, Young-Jun et al. | Springer Verlag | 2006


    Experimental study on durability comparison of the GFRP decks by resin types

    Park, Ki-Tae / Hwang, Yoon-Koog / Lee, Young-Ho et al. | Springer Verlag | 2007


    Progressive fracture in composites subjected to hygrothermal environment

    MINNETYAN, LEVON / MURTHY, PAPPU / CHAMIS, CHRISTOS | AIAA | 1991