A Ni-Cd alloy plating is applied to the surface of steel component by brush plating, which can realize the double protection of sacrificial anode by cathodic protection and mechanical protection. The effect of concentration of Cd2+ in plating solution on the corrosion resistance of the plating was studied by using the control variable method. The corrosion potential, polarization resistance and corrosion resistance of the coating with different concentrations of Cd2+ were measured by polarization curve, AC impedance spectroscopy, full immersion corrosion test and salt solution immersion test. The results show that the co-deposition of Ni-Cd alloy with Cd of mass fraction of 15%-90% can be realized when the mole fraction of Cd2+ changes from 0.5%-5%, which belongs to abnormal co-deposition. When the molar fraction of Cd2+ is 4 %, that is, the mass fraction of Cd2+ in the coating is 69.40 %, and the corrosion resistance of the alloy brush coating is the best.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Cd content in Ni-Cd alloy plating on corrosion resistance of the plating


    Beteiligte:
    YAN Baoqiang (Autor:in) / FEI Jingyin (Autor:in) / ZHANG Man (Autor:in) / WANG Jun (Autor:in) / HAN Xizheng (Autor:in) / ZHAO Lina (Autor:in)


    Erscheinungsdatum :

    2022




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Plating, Zinc-Nickel Alloy

    SAE Technical Papers | 2004


    Plating, Zinc-Nickel Alloy

    SAE Technical Papers | 2001


    Plating, Tin-Zinc Alloy

    SAE Technical Papers | 2011


    Plating, Tin-Zinc Alloy

    SAE Technical Papers | 1999


    Plating, Zinc-Nickel Alloy

    SAE Technical Papers | 2020