The mechanical and high-temperature dielectric properties of SiCf/SiC composites with nano-SiO2 filler were investigated in the present work for the development of high-temperature structural microwave absorbing materials. The results reveal that the flexural strength of SiCf/SiC composites is increased firstly and then is degraded with the filler content increased from 3% to 15%, and the maximum strength can be up to 275 MPa, meanwhile all of which show favourable fracture toughness. Owing to the high specific surface area and low permittivity of SiO2 filler, the complex permittivity of the composites decreases and the room-temperature reflection loss (RL) is promoted with the increase of filler content. When the composites possess 15% SiO2 filler, the room-temperature RL values can be reached to –8 dB in the whole X band with the thickness of 3.2-4.0 mm. The complex permittivity of the composites increases with the rising temperatures, while the specific values and increasing range of the high-temperature complex permittivity can be significantly reduced by introducing the SiO2 filler, and the composites can obtain excellent microwave absorbing property at 700 ℃ with the thickness range of 2.7-3.0 mm.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Mechanical and High-temperature Dielectric Properties of SiCf/SiC Composites with SiO2 Filler


    Beteiligte:
    MU Yang (Autor:in) / DENG Jiaxin (Autor:in) / LI Hao (Autor:in) / ZHOU Wancheng (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt





    Effect of Fabric Preform Structure on Mechanical Properties of SiCf/PyC/SiBCN Composites

    TAN Xi / LIU Wei / CAO Lamei et al. | DOAJ | 2017

    Freier Zugriff

    Interphase optimization of SiCf/Si3N4 composites

    DENG Yangfang / CHEN Xu / WANG Tongtong et al. | DOAJ | 2023

    Freier Zugriff

    Research progress on meso-structure and mechanical properties of SiCf/SiC textile composites

    YANG Tiantian / ZHANG Diantang / QIU Haipeng et al. | DOAJ | 2020

    Freier Zugriff

    Performance of SiC whisker reinforced SiCf/SiC composites fabricated by PIP

    JIANG Zhuoyu / LYU Xiaoxu / ZHOU Yiran et al. | DOAJ | 2021

    Freier Zugriff