Li1.3+xAl0.3-xCoxTi1.7(PO4)3 (x=0, 0.04, 0.08, 0.12) ceramics were prepared by high temperature solid-state method. The effects of Co2+ ion doping content on the morphology, phase, ion conductivity, dielectric property and microwave absorption property were studied. Results show that Li1.3+xAl0.3-xCoxTi1.7(PO4)3 ceramics had cubic grains with relative densities of 90%, and they are single rhombohedral LiTi2(PO4)3 phase without any impurity. Li1.34Al0.26Co0.04Ti1.7(PO4)3 ceramic has the highest ionic conductivity of 1.14×10−3 S·cm−1. A lower valent cation occupying the Ti(Al) site can reduce the coulombic repulsion between Li+ ions and skeleton ions, and appropriate doping content can obtain suitable size of Li+ ions channel. Then, Li+ ion has a minimum activation energy of 0.29 eV, which is easy to generate thermal ion relaxation polarization. Therefore, Li1.34Al0.26Co0.04Ti1.7(PO4)3 ceramic also has the highest complex permittivity, ε' is 12.9-13.7 and ε" is 3.1-3.8. In addition, due to the combined effect of polarization loss and conductance loss, it has the optimum microwave absorption property of an absorption bandwidth covering the whole X-band and a minimum reflection loss of −17.3 dB at 9.67 GHz, which is a potential candidate of high-temperature lightweight microwave absorption material.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effects of Co2+ ion doping content on conductivities and microwave absorption properties of Li1.3+xAl0.3-xCoxTi1.7 (PO4)3 ceramics


    Beteiligte:
    CHEN Dan (Autor:in) / ZHOU Yingying (Autor:in) / YANG Xin (Autor:in) / CAO Nannan (Autor:in) / ZHANG Jieyong (Autor:in) / YANG Jilong (Autor:in)


    Erscheinungsdatum :

    2022




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Measuring Microwave Conductivities Of Superconducting Films

    Bhasin, K. B. / Warner, J. D. / Miranda, F. A. et al. | NTRS | 1993



    Preparation and microwave absorption properties of Fe3+ doped LaNiO3 perovskite ceramics

    YU Man / ZHOU Yingying / YING Kairui et al. | DOAJ | 2023

    Freier Zugriff

    Doping mechanisms and electrical properties of La-doped BaTiO3 ceramics

    Morrison, F. D. / Sinclair, D. C. / West, A. R. | British Library Online Contents | 2001