The ultrasonic vibration (UV) treatment has been successfully applied to improve the particles distribution of nano-SiCp reinforced Al-5Cu composites fabricated by combined processes of dry high energy ball milling and squeeze casting. Large particles aggregates are eliminated by effects of the cavitation and the acoustic streaming of UV for 1 min. All the particles aggregates are eliminated and the particles are uniformly distributed in the melt after treated by UV for 5 min. The ultimate tensile strength, yield strength and elongation of the 1%(mass fraction) nano-sized SiCp/Al-5Cu composites treated by UV for 5 min are 270 MPa, 173 MPa and 13.3%, which are increased by 7.6%, 6.8% and 29% compared with Al-5Cu matrix alloy, respectively, and are increased by 27.4%, 9.5% and 303% compared with the untreated composites, respectively. The improvements of mechanical properties after UV are attributed to the uniform distribution of reinforcement and grain refinement of aluminum alloy matrix.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Ultrasonic Vibration on Microstructure and Mechanical Properties of Nano-SiCp/Al-5Cu Composites


    Beteiligte:
    LI Jianyu (Autor:in) / LYU Shulin (Autor:in) / WU Shusen (Autor:in) / LU Kang (Autor:in) / GAO Qi (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Processing, Microstructure and Mechanical Properties of SiCp/AZ91 Mg Matrix Composites Fabricated by Squeeze Casting

    Qiu, X. / Wang, X. J. / Zheng, M. Y. et al. | British Library Conference Proceedings | 2007


    Microstructure, mechanical properties and work hardening behavior of SiCp/2024Al composite sheet

    XUE Pengpeng / CAO Fuxiang / DENG Kunkun et al. | DOAJ | 2023

    Freier Zugriff



    Effects of Processing on the Properties of A356 Al-20 vol.% SiCp and AZ91 Mg-20 vol.% SiCp Composites

    Altmisoglu, A. / Rozak, G. A. / Wallace, J. F. et al. | SAE Technical Papers | 1993