Sn-58Bi-xY alloys with different Y contents (x = 0.0%, 0.1%, 0.2%, 0.3%, 0.4%, 0.5% (mass fraction, the same below )) were fabricated in a vacuum furnace in nitrogen atmosphere. Microstructure, phase composition, melting characteristic, wettability and hardness of the alloys were investigated, and the influence of the rare earth Y on the formation of intermetallic compound among Sn-58Bi/Cu were analyzed, and the shear strength were test. The results show that the Sn-Bi microstructure is refined, and the microstructure of Sn-58Bi-xY is rich in Sn phase, Bi phase and eutectic microstructure of layered structure. The rare earth Y is distributed in rich Bi phase evenly. The melting points and melting ranges are less affected with the Y addition. The wettability of Sn-58Bi alloys reduces when the Y contents increase, but the hardness of Sn-58Bi alloys increases and reaches the maximum value 24.18HV when the content of Y is 0.4%. Rare earth Y can improve the shear strength of Sn-58Bi-xY/Cu solder joints, and the shear strength of the joints reach the maximum value 53.55 MPa when the content of Y is 0.2%. Y can promote the reaction of Sn-58Bi solder with Cu during welding and forming Cu6Sn5 intermetallic compound.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Rare Earth Y on Microstructure and Properties of Sn-58Bi Solder Alloy


    Beteiligte:
    GONG Liukui (Autor:in) / LIAO Jinfa (Autor:in) / YUAN Jihui (Autor:in) / LI Guihe (Autor:in) / CHEN Huiming (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Effect of CeCl~3-Containing Flux on Microstructure and Mechanical Properties of Mg Alloy Containing Rare Earth

    Ding, W. J. / Wu, G. H. / Bong, S. Y. et al. | British Library Conference Proceedings | 2007


    Rare Earth Conversion Coating of Magnesium Alloy AZ91D

    Bai, L. Q. / Li, D. / Guo, M. et al. | British Library Conference Proceedings | 2007


    Effect of rare-earth element in laser cladding high-temperature alloy [3862-126]

    Tian, N. / Yang, Y. / Yang, B. et al. | British Library Conference Proceedings | 1999


    Bending properties and failure mechanism of fiber rare earth magnesium alloy super hybrid laminates

    ZHAO Zong / ZHENG Xingwei / QIAN Renfei et al. | DOAJ | 2021

    Freier Zugriff