Electric spark deposition (ESD) combining with micro-arc oxidation (MAO) were employed to fabricate ZrO2/NiCrAlY thermal barrier coating (TBC) on GH4169 substrate. Firstly, a NiCrAlY coating with thickness of 250 μm was deposited on GH4169 substrate by ESD. Secondly, a Zr coating with thickness of 150 μm was deposited on NiCrAlY coating followed by MAO of the Zr coating. The thermal shock performances of the coatings under different temperatures were investigated. The results indicate that the thermal cycle numbers of the coatings at 750℃, 850 ℃ and 950℃ are 51, 32, and 19 respectively.
Preparation and Thermal Shock Performance of ZrO2/NiCrAlY Thermal Barrier Coating
2017
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Thermal shock testing of thermal barrier coating/bondcoat systems
Tema Archiv | 2004
|Thermal and Structural Analysis of Functionally Graded NiCrAlY/YSZ/Al2O3 Coated Piston
SAE Technical Papers | 2015
|Thick thermal barrier coating ( TTBCs )
Kraftfahrwesen | 1995
|Enhanced zirconia thermal barrier coating systems
Online Contents | 2006
|Corrosion-resistant ceramic thermal barrier coating
NTRS | 1980
|