Graphene oxide (GO) modified epoxy resin (GH81) was prepared by mechanical grinding, and the dispersion of GO in the epoxy resin (H81) was analyzed by optical microscope, while the melting performances and curing behaviors of H81 and GH81 were researched through rheometer and differential scanning calorimeter respectively. The results show that GO is uniformly dispersed into the matrix resin,and the addition of GO hardly affects the melt viscosity and curing condition of the matrix resin at all. In addition, the 0° tensile strength, bending strength and compression strength of GH81 based carbon fiber reinforced composite (GH81-300) are 2270 MPa, 2239 MPa and 1529 MPa respectively, which is increased by 6.4%, 7.2% and 7.1% respectively, as compared with that of composite without GO.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Properties of graphene oxide modified epoxy resin and its composites


    Beteiligte:
    REN Zhidong (Autor:in) / HAO Sijia (Autor:in) / XING Yue (Autor:in) / YANG Cheng (Autor:in) / DAI Shenglong (Autor:in)


    Erscheinungsdatum :

    2019




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Mechanical and thermal properties of epoxy composites containing graphene oxide and liquid crystalline epoxy

    Qi, B. / Yuan, Z. / Lu, S. et al. | British Library Online Contents | 2014


    Enhanced thermal properties for epoxy composites with a three-dimensional graphene oxide filler

    Gao, J. / Yu, J. / Wu, X. et al. | British Library Online Contents | 2015


    Epoxy-modified cyanate ester resin and its high-modulus carbon-fiber composites

    Ren, Penggang / Liang, Guozheng / Zhang, Zengping | Tema Archiv | 2006


    Potential use of graphene composites in epoxy resin as anticorrosive painting in automotive industry

    de Oliveira, Elisa M. N. / Hurtado, Luiz P. / Sormani, Mariana B. et al. | SAE Technical Papers | 2024


    Preparation and Cryogenic Properties of Cyanate Ester Resin Blends Co-modified by Phenoxy Resin/Epoxy Resin

    ZHANG Haiqi / WANG Guan / GAO Tangling et al. | DOAJ | 2018

    Freier Zugriff