The strain controlled low cycle fatigue (LCF) and creep-fatigue interaction (CFI) tests of a TiAl alloy were conducted at 750 °C in air. The strain ratio, strain amplitude and strain rate were –1, 0.4% and 1 × 10–3 s–1 respectively. The high temperature LCF and CFI stress-strain stable hysteresis loop, cyclic hardening/softening, mean stress relaxation and life were studied and compared in details. Morrow modified method and unified life model developed in the present study were employed to predict the fatigue life for LCF and CFI life of TiAl alloy. Finally, the failure mechanisms between LCF and CFI specimens were compared, and some interesting conclusions were obtained. The results show that: (1) there are obvious differences on stress-strain stable hysteresis loop, cyclic hardening/softening, mean stress relaxation and life between LCF and CFI tests; (2) Morrow modified method is not able to predict the fatigue life for LCF and CFI life for TiAl alloy, however, the predicted fatigue life by the unified life model is located in the scatter band of ± 1.5; (3) the fatigue cracks are initiated from the surface for all of LCF and CFI specimens, and LCF specimens show more transgranular appearance while CFI specimens show obvious mixed appearance of both transgranular and intergranular.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    High temperature fatigue-creep interactive behavior and life prediction of a TiAl alloy


    Beteiligte:
    DONG Chengli (Autor:in) / HU Xiaoan (Autor:in)


    Erscheinungsdatum :

    2020




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Statistical Distribution of Fatigue Life for Cast TiAl Alloy

    WAN Wenjuan / HAN Bo / HAN Wei et al. | DOAJ | 2016

    Freier Zugriff

    Creep Behavior of Cast TiAl Base Intermetallics

    Kim, S. / Cho, W. / Hong, C.-P. et al. | British Library Conference Proceedings | 1993



    A unified criterion for fatigue–creep life prediction of high temperature components

    Zhu, Shun-Peng / Yang, Yuan-Jian / Huang, Hong-Zhong et al. | SAGE Publications | 2017


    High Temperature Low Cycle Fatigue Properties and Failure Mechanism of a TiAl Alloy

    DONG Chengli / YU Huichen / JIAO Zehui et al. | DOAJ | 2017

    Freier Zugriff