Flaw tolerance performance of TC4 alloy was investigated for helicopter transmission systems design. The impact pit flaws and scratch flaws were investigated by fatigue specimens with same flaw depth for flaw tolerance design,and high-cycle fatigue S-N curve tests were conducted. The results show that both scratch flaws and impact pit flaws significantly reduce the fatigue limit of the TC4 titanium alloy. The scratch flaw has a higher flaw influence factor(Kflaw) of 2.29 compared to the impact pit flaw’s Kflaw value of 1.75 under the same flaw depth conditions. Fracture surface analysis provided laws of the fatigue crack initiation and propagation associated with these flaws. Scratch flaws mainly exhibit multiple sources,with crack initiated at the root of the scratch,while the characteristics of fatigue crack initiation for impact pit flaws vary with the applied stress. Multiple sources are observed under high stress lever,with crack initiated on the surface of the pit,while under low stress,the crack initiates at a subsurface of the pit.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Flaw tolerance performance of TC4 alloy used in transmission system


    Beteiligte:
    CHEN Xin (Autor:in) / ZHAO Yongming (Autor:in) / ZHAO Chunling (Autor:in) / YE Xubin (Autor:in) / XU Wei (Autor:in) / HE Yuhuai (Autor:in)


    Erscheinungsdatum :

    2024




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Flaw Tolerance Evaluation of Helicopter Rotor Parts

    Beretta, S. / Giglio, M. / Mariani, U. et al. | British Library Conference Proceedings | 2004


    Flaw Tolerance Assessment of Rotorcraft for Civil Certification

    Mariani, U. / Vicario, M. / International Committee on Aeronautical Fatigue | British Library Conference Proceedings | 2005


    Application of Flaw Tolerance Methodologies to Rotorcraft Fatigue Qualification

    Mariani, U. / Royal Aeronautical Society | British Library Conference Proceedings | 2005



    Flaw tolerance in lap shear brazed joints - Part 1

    Flom, Y. / Wang, L. | Tema Archiv | 2004