In this study; brake discs used in vehicles have investigated. The behavior of these discs during braking, wear and braking distance performance of the coated and uncoated surfaces during the braking process were evaluated. The surface of the commercially produced discs was coated with a thickness of 1 mm using the HVOF (High Velocity Oxy-Fuel) coating method. In the coating process CoNiCrAlY, WC-Co (88/12), NiCrBSi and MoNiCrBSiFe (Mo 25%) 4 (four) different ceramic powders were used respectively. Wear and brake distance tests of coated and uncoated discs were performed by braking in a total of 20 brakes in 15 seconds on the brake-suspension tester. After the brake tests, the surface roughness changes of the discs, surface hardness change, mass loss and the abrasion values on the disc surfaces were determined due to the brake force applied to the discs during the experiment. The most wear on the discs was on the CoNiCrAlY ceramic powder coated disc at 0,4 g, while the least wear occurred on the disc coated with NiCrBSi ceramic powder at 0,2 g.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Experimental Investigation of the Effect of Brake Disconnished by Hvof Method


    Beteiligte:


    Erscheinungsdatum :

    2019




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Computational and experimental investigation of High-Velocity Oxygen-Fuel (HVOF) thermal spraying

    Hassan, Basil / Oberkampf, William / Neiser, Richard et al. | AIAA | 1996



    Experimental investigation of disc brake friction

    Ilm,A. / Leung,P.S. / Datta,P.K. et al. | Kraftfahrwesen | 2000


    An experimental investigation into drum brake squeal

    Lang,A.M. / Newcomb,T.P. / Mintex don,GB et al. | Kraftfahrwesen | 1989


    An experimental investigation into drum brake squeal

    Lang, A.M. / Newcomb, T.P. | Tema Archiv | 1989